1.1121對應牌號
更新時間：2022-03-07
點擊次數：1138
| Elements not quoted in this table shall not be intentionally added to the steel without the agreement of the purchaser, other than for thepurpose of finishing the heat. Steels with improved machinability as a result of the addition of lead or higher sulfur contents, depending on the manufacturing process up to around 0.1 % S, may be supplied on request. In this case, the upper limit of the manganese content may be increased by 0.15 % |
| C | Si | Mn | P | S |
| 0.07 - 0.13 | max 0.4 | 0.3 - 0.6 | max 0.035 | max 0.035 |
| Rm - Tensile strength (MPa) (+A) | 430 |
| Rm - Tensile strength (MPa) (+CR) | 830 |
| Rp0.2 0.2% proof strength (MPa) (+A) | 345 |
| A - Min. elongation Lo = 80 mm (%) (+A) | 26 |
| Brinell hardness (HBW): (+A) | 131 |
| Brinell hardness (HBW): (+N) | 85 - 140 |
| Rockwell B hardness ( HRB or RB): (+A) | 73 |
| Vickers hardness ( HV): (+) | 135 |
| Vickers hardness ( HV): (+CR) | 250 |
| Weldability: It is a soft carbon-steel, easily cold machinable and weldable without any particular precautions. |
| EU EN | Germany DIN,WNr | France AFNOR | England BS | Italy UNI | Spain UNE | Russia GOST | Inter ISO | |||||||||||||
| C10E |
|
|
|
|
|
|
|